 VOLGAMID 尼龙66增强系列 |
|
|
Technical data sheet |
|
VolgamidÒPA66G25NC201
25%玻纤增强尼龙66
25% glass fiber reinforced PA66 |
|
项目Item |
典型性能Typical Characteristic |
测试标准Testing Standard |
|
值Value |
单位Unit |
|
机械性能Mechanical Properties |
|
|
|
|
拉伸强度Tensile Strength |
165 |
MPa |
ISO527, 50mm/min |
|
断裂伸长率Elongation at break |
3.0 |
% |
ISO527, 50mm/min |
|
弯曲强度Flexural Strength |
240 |
MPa |
ISO178, 2mm/min |
|
弯曲模量Flexural Modulus |
7290 |
MPa |
ISO178, 2mm/min |
|
简支梁缺口冲击强度
Charpy Impact notched |
11.1 |
KJ/m2 |
ISO179/1eA |
|
简支梁无缺口冲击强度
Charpy Impact unnotched |
68.6 |
KJ/m2 |
ISO179/1eU |
|
洛氏硬度Rockwell Hardness |
119 |
|
ISO2039/2 |
|
热性能Thermal Properties |
|
|
|
|
热变形温度
Temp. of deflection under load (0.45MPa) |
|
℃ |
ISO75 |
|
热变形温度
Temp. of deflection under load (1.80MPa) |
252 |
℃ |
ISO75 |
|
熔点Melting Point |
260 |
℃ |
ISO3146C |
|
电性能Electrical Properties |
|
|
|
|
体积电阻率Volume Resistant |
|
ohm*m |
IEC60093 |
|
表面电阻率Surface Resistant |
1013 |
ohm |
IEC60093 |
|
介电强度Dielectric Strength |
|
KV/mm |
IEC 60243-1 |
|
电痕化指数Comp Track Index |
|
V |
IEC 60112 |
|
其它Others |
|
|
|
|
密度Specific Gravity |
1.32 |
g/cm3 |
ISO1183 |
|
灰分Ash Content |
25±2 |
% |
ISO3451-4 |
|
熔体流动速率（250℃,2.16kg）
Melt flow rate |
|
g/10min |
ISO62 |
|
吸水率Water Absorption |
1.3 |
% |
ISO62 |
|
吸湿率Humidity Absorption |
|
% |
ISO62 |
|
模塑收缩率Mold Shrinkage |
0.3/0.9 |
% |
ISO294-4 |
|
燃烧性能 |
|
|
|
|
UL垂直燃烧Flammability |
HB |
mm/Class |
UL-94 |
|
灼热丝可燃指数
Glow-wire Flammability Index |
|
mm/℃ |
IEC 60695-2-12 |
|
Disclaimer：Unless specified to the contrary, the value given have been established on standardized test specimens at room temperature.The figures should be regarded as guide values only and not as binding minimum value. Kindly note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mould/die, the processing conditions and the colouring. |  下载PDF文档 |
|
|
|
|
|